Eliminating Die Marks On Metal Bending When Using A Press Brake
Bending pre-painted sheet metal parts or parts that are made of aluminum, stainless steel, brass, copper and other materials that are not going to be painted is likely to cause die marks. And the odds are good that customers will not accept them. Die marking is an age-old problem that historically had fairly limited solutions, and even those often compromised press brake productivity.
An early solution to alleviate this problem was to use press brake die holders made from steel or aluminum that utilized a polyurethane pad, which served as the die. This method normally worked well – and still does – in eliminating die marks, but it comes with several inherent problems. They include the deterioration of the polyurethane pad during use, which creates the need for frequent angle adjustments. In addition, the pad tends to collect grit or debris that might find its way onto the sheet metal. As the residue becomes embedded in the pad, it causes die marking.
Also, because of the resistance that is caused by pushing the material into the polyurethane pad, the bending tonnage requirements to form the part increase significantly and reach very high tonnage levels. This is true when bending parts with tooling that presents a large surface area, such as large radius punches. And finally, polyurethane pads are expensive to use, especially when bending long parts as they have a fairly short life.
Another frequently used solution is polyurethane sheeting, which is typically sold in rolls of varying widths and thicknesses, in 100-ft. lengths, and in some cases by the foot. This product is normally attached to the ends of the die via C-clamps. When longer lengths are used, the center is normally secured to the die via duct tape, masking tape or similar adhesive tapes.
Polyurethane sheeting works well in preventing die marks, especially when used with a die that has large shoulder radii. However, the thickness of the sheeting reduces the width of the V-opening on the die and in doing so, can create the need to alter the blank size.
As it is draped over the die and clamped in place, the polyurethane sheeting must also be stretched to the bottom of the stroke with each bend, which increases the tonnage that is required to form the part. The combination of the material passing over the sheeting during bending and the stretching that the sheeting undergoes with each bend causes it to quickly wear. This creates the need for the press brake operator to frequently unclamp the sheeting and move the roll forward the length of the die to present a fresh section of sheeting over the shoulder radii of the die. While producing favorable parts, this process can be taxing on press brake productivity.
As an alternative solution, many press brake tooling manufacturers have added dies to their product lines that feature large shoulder radii on the V-openings. This eliminates the initial and, often, the most damaging stage of die marking – the gouging that occurs when dies with small shoulder radii on the V-openings penetrate the material during bending. As the material is pushed deeper into a V-opening, the V-opening with small shoulder radii penetrates and pushes through the material and leaves unsightly grooves or impressions in the material along with aggressive marks caused when the material is dragged over the sharp shoulder radii.
On dies with larger shoulder radii, normally 1.5 times the material thickness or greater, the shoulder radii do not penetrate the material. This makes it possible for the material to glide over the shoulder radii and eliminate the worst of the die marking. This places a premium on the need for dies with precision ground shoulder radii that are hardened and have very fine surface finishes.
While material gouging is eliminated by the larger shoulder radii, that isn’t the only area of concern. A second stage of die marking is likely to occur. The material can be marred by metal-to-metal contact that occurs as the material slides over the shoulder radii on the die.The only way to eliminate the die marking that is created during this stage of bending is to place a protective barrier between the material and the die.
A better solution
A recent development in the fight against die marking is the use of a densely woven nylon cloth frequently referred to as “No-Mar Cloth.” Unlike polyurethane sheeting, the No-Mar Cloth is much harder and, therefore, far more durable, providing a usable life cycle as much as ten times longer than polyurethane sheeting. Being of a harder and denser material, it does not need to be stretched to the bottom of the stroke with every bend.
This increases its life, reduces the number of times that it must be moved and eliminates the negative effect that polyurethane sheeting has on tonnage requirements. Like polyurethane sheeting, its life is greatly enhanced when using dies with large shoulder radii.